  CHARACTERISTICS OF PARTICLEBOARD MADE FROM SEDAR CHIPS AND WOOD SLABS (TECHNICAL NOTE)
 
S. M. Hosseini and M. Fadaei
 
( Received: October 13, 2012 – Accepted: November 15, 2012 )
 
 

Abstract    This study was Characteristics of manufacture particleboard (PB) from sedar and wood slab of impregnated with UF. The chips were divided into coarse chips with dimensions of 2-4 mesh and fine chips of 30–60 mesh, urea formaldehyde (UF) resin solution at concentrations of 45 %, and 55% sprayed on these chips about 1 min until 10% to dry weight chips, they were dried under 5% moisture in a dram dryer before impregnated with resin. Three-layer mats with target densities of 0.70 g/cm3 were formed by using fine chips for the face layer (20%) and back layer (20%) and coarse chips for the core layer (60%). A conventional hot press was used for fabrication of the PB, and the temperature, pressure and pressing time were 2.7 MPa, and 240 sec, respectively. The nominal dimensions of particleboard were 3660×1830×16 mm (thick).Result showed that the mechanical properties of PB increased with an increase in the percent of UF. Their represented could by efficacy between proportion of sedar with slab, Also percent of surface with core layers. The bending strength, internal bonding strength, and thickness swelling (%) of the UF-impregnated particleboards exhibited excellent performances compared to those made in the past

 

Keywords    Mechanical properties, Thickness Swelling, Particleboard, Sedar, Slab

 

چکیده    در این تحقیق خصوصیات تخته خرده چوب ساخته شده از چوب سوزنی برگان در مخلوط با چوب ضایعاتی پشت لا آغشته شده با چسب اوره فرمالدهید مورد بررسی قرار گرفت. ذرات آماده برای لایه میانی با مش 2 تا 4 و برای لایه سطحی با مش 30 تا 60 انتخاب شدند. غلظت چسب برای لایه سطحی 45 و لایه میانی 55 درصد انتخاب شد. چسب با نسبت 10 درصد نسبت به وزن ذرات چوب با رطوبت 5 درصد اضافه شد.کیک 3 لایه با نسبت 60 درصد برای لایه میانی و 2 لایه سطحی (هر کدام 20 درصد برای ساخت تخته خرده چوب با دانسیته 7/0 گرم بر سانتی متر مکعب انتخاب شد. مولفه های پرس با زمان 240 ثانیه و فشار 2.7 مگاپاسکال تعیین شد. ابعاد تخته16×3660×1830 میلیمتردر نظر گرفته شد. نتایج نشان دادند خصوصیات مکانیکی محصول با افزایش چسب بهبود می یابد. این اثر می تواند تحت تاثیر نسبت ضایعات پشت لا با چوب سوزنی برگ و اثر نسبت لایه سطحی به میانی تخته باشد.

References   

1.        FAO, Report of Agriculture and Natural Resources, 2011.

2.        Wang, D. and Sun, X.S., “Low density particleboard from wheat straw and corn pith”, Industrial Crops and Products, Vol. 15, (2002), 47–50.

3.        Ross, R.J. and Pellerin, R.F., “NDE of wood based composites with longitudinal stress wave”, Forest Products Journal, Vol. 38, (1988), 39–45.

4.        Sun, Y.C. and Arima, T., “ Structural mechanics of wood composite material: ultrasonic evaluation of internal bond strength daring an accelerated aging test”, Journal of Wood Science, Vol. 44, (1998), 348–53.

5.        Industrial Pollution Control Corps (IPCC), “Recycle and reuse of wood-waste materials”, Taipei, Taiwan, Industrial Development Bureau Ministry of Economic Affairs, (1996), 15–41.

6.        European Committee for Standardization (CEN), DIN EN 317, “Particleboards and fiberboards- Determination of swelling in thickness after immersion in water”, (1993).

7.        European Committee for Standardization (CEN), DIN EN 622-5, “Wood based panels- Determination of modulus of elasticity in bending strength”, (1997).

8.        Yang, T.H., Tsai, M.J. and Wang, S.Y., “Characteristics of OSB made from PFresin impregnated flakes”, Forest Products Industries, Vol. 20, (2001), 227–37.

9.        Yang, T.H., Chen, B.J. and Wang, S.Y., “Properties of the light weight OSB made from PF-resin impregnated flakes”, Forest Products Industries, Vol. 21, (2002), 39–50.

10.     Wong, E.D., Zhang, M., Wang, Q. and Kawai, S., “Formation of the density profile and its effects on the properties of particleboard”, Wood Science and Technology, Vol. 33, (1999), 327–40.

 

11.     Wong, E.D., Yang, P., Zhang, M., Wang, Q., Nakao, T. and Li, K.F., “Analysis of the effects of density profile on the bending properties of particleboard using finite element method (FEM)”, Holz als Roh-und Werkstoff, Vol. 61, (2003), 66–72.

12.     Yang, T.H., Chen, H.C., Wang, S.Y. and Tsai, M.J., “Characteristics of veneer overlaid OSB by using nondestructive test method”, Quarterly Journal of Chinese Forestry, Vol. 36, (2003), 199–209.

13.     Ayrılmıs, N., Kartal, S.N., Laufenberg, T.L., Winandy, J.E. and White, R.H., “Physical and mechanical properties and fire, decay, and termite resistance of treated oriented strandboard”, Forest Products Journal, Vol. 55, (2005), 74–81.

14.     George, I.M. and Antonios, N.P., “Reducing the thickness swelling of wood based panels applying a nanotechnology compound”, Springer, verlag, (2010).

15.     Rowell, R. and Levan, S.L., “Thermal Properties, Hand book of Wood Chemistry and Wood Composites”, CRC Press, ISBN, 0-8493-1588-3, (2006), 121-138.

16.     Oh, Y.S., Cha, J.K., Kwak, J.H., “Properties of particleboard from Korea pruning logs”, Forest Product Journal, Vol. 53, (2003), 67–69.

Wang, S.Y., Chen, B.J., “Studies on the application of Japanese-Fir particle for the improvement of domestic particleboard processing properties”, Forest Products Industries, Vol. 5, (1986),2-14.


Download PDF 



International Journal of Engineering
E-mail: office@ije.ir
Web Site: http://www.ije.ir